比较几种红木石蜡油浴后顺纹抗压强度、接触角变化的研究综述

摘要:红木因其独特的颜色和纹理，质地细腻，材质坚硬，所制成的工艺品及家具具有很高珍藏价值和经济价值，深受人们喜爱。本文采用石蜡油浴热处理的方法对红木类（花梨，大红酸枝，酸枝，血檀）进行处理，研究了热处理前后其顺纹抗压强度和表面接触角变化。处理前后的木材变化直接影响家具的使用，这些性能参数对于实际生产很有意义。

关键词：红木；石蜡油；热处理；顺纹抗压强度；表面接触角

A review on the change of the compressive strength and contact angle of several kinds of red - wood stone oil baths

overview

Abstract: Because of its unique color and texture, fine texture, hard material, the handicrafts and furniture made by it have high value of treasure and economic value, and are loved by people. In this paper, the method of heat treatment in paraffin oil bath is used to treat the red wood (pears, pears, pears, pears, pears, pears, pears, pears, pears, etc.). The changes of compressive strength and surface contact angle before and after heat treatment were studied. The treated wood directly affected the use of furniture. These performance parameters were of great significance for practical production.

Key words: Mahogany; paraffin oil; heat treatment; conformable compressive strength; surface contact angle

1. 木材油浴热处理研究的目的意义

在我国红木资源稀缺，红木作为一种天然高分子的有机体，因其独特的颜色和纹理，质地细腻，材质坚硬，所制成的工艺品及家具具有很高珍藏价值和经济价值，深受人们喜爱。然而自身存在着些不良的固有特性性。其中木材的湿胀干缩性以及由于各向尺寸变化不一 致而引起的翘曲、开裂等种种变形引起的物理力学性质的改变影响木材加工、利用和木制品寿命等一系列的问题[1]。许研究者直在努力研究和积极探索使木材尺寸稳定化的方法，积累了经验，取得了效果。而石蜡是非极性物质，通过石蜡的改性处理后的木材表面接触角直接影响到家具表面涂饰。正因如此，石蜡油浴改性对其物理力学性能的影响尤为重要。

1. 木材油浴热处理的研究进展概况

2014年南京理工大学范敏，倪欧琪等人以甲基硅油为热处理介质对东非黑黄檀进行热处理，研究了热处理前后红木的抗压强度。试材为含水率3.33%的东非黑黄檀的心材 ，尺寸为20*20*30，处理温度(140、160、180、200、 220 ℃ ) 和处理时间(2.5、3、3.5、4、4.5 h) 均设定为5个水平。每次处理1个试材，每个实验重复4次。以甲基硅油为介质进行常压热处理。首先升温到目标温度，稳定0.5h，然后将试材没入油浴中，按要求保温相应的时间后取出，待冷却至室温之后将木材置于正己烷溶剂中浸泡 20 min，溶解掉木材表面残留的硅油，然后再将木材置于40℃环境中挥发表面的残留溶剂。取试样的中间部分.按照国家标准GB 1935—1991《木材顺纹抗压强度试验方法》测定。研究表明：与未处理材比较，热处理温度为160℃时抗压强度提升最大(44.1%)，继续升温其抗压强度有下降趋势[2]。